PA66+15-GF-的物性表

物性表TECHNICALDATASHEETVersione1Aggiornata:27/05/11这里提供的信息是出于善意，仅供参考。所有项目要求的特性应认真评估。参数值为成型样品在40小时，23摄氏度和50%相对湿度条件下测得。除非另外声明，这些产品不适合用于食品和或医疗应用。他们不应以任何方式被视为对我方部件的正式承诺或保证，尤其是由于第三方对我们产品的不正确使用。Theinformationcontainedhereinaresuppliedingoodfaithandgivenpurelyasanindication.Propertiesshouldbecarefullyevaluatedforallprojectsrequirements.Valuesarereferredtomouldedsamplesconditionedfor40h-23°C-50%U.R.Unlessotherwisepostedthisproductisnotsuitableforfoodand/ormedicalapplicationanduse.Theyshallnotbeconsideredinanywayasaformalcommitmentorwarrantyonourpartespeciallyincaseofimproperuseofourproductsfromthirdparties.SCTREV.1DEL01/01/11POLIMIDA15GFNATURALPA66–15%玻纤PA66–15%GLASSFIBRE特性Properties标准Standard单位Unit典型值TypicalValues物理和热/PHYSICAL&THERMAL密度DensityISO1183g/cm³1.25熔点MeltingPointDSC°C260成型收缩率(均值)MoldShrinkage(average)-%0.6–1.0吸湿率(浸水)MoistureAbsorption(waterimmersion)23oC-24hISO62%1.0熔流指数MeltFlowIndexISO1133g/10min-维卡软化温度VicatSofteningTemperature50°C/h-10NISO306°C255热变形温度HeatDeflectionTemperature0,45MPaISO75-2°C250热变形温度HeatDeflectionTemperature1,80MPaISO75-2°C240耐热/球压测试HeatResistance/BalltestIEC335-1IEC60695-10-2°C165连续使用温度(无负载)ContinuousUseTemperature(withoutload)-°C110机械/MECHANICAL屈服拉伸强度TensileStrengthatYieldISO527MPa125断裂拉伸强度TensileStrengthatBreakISO527MPa125拉伸模量TensileModulusISO527MPa6800屈服拉伸应变TensileStrainatYieldISO527%4.5断裂拉伸应变TensileStrainatBreakISO527%4.5悬挂梁缺口冲击强度Izod-NotchedImpactStrengthISO180/AKJ/m²7.5悬挂梁无缺口冲击强度Izod-UnnotchedImpactStrengthISO180/UKJ/m²40电气和可燃性/ELECTRICAL&FLAMERETARDANCY相对起痕指数(CTI)ComparativeTrackingIndex(CTI)IEC60112V500阻燃性Flammability3,2/1,6/0,8mmUL94-HB灼热丝点火温度(GWT)GlowWireFlammabilityTemperatureGWFI-2mmIEC60695-2-12°C650灼热丝点火温度(GWT)GlowWireIgnitionTemperatureGWIT-2mmIEC60695-2-13°C-成型条件(建议)/Moldingconditions(suggested)干燥温度DryingTemperature≥3h/90-100oC成型温度Moldingtemperature270-290oC模具温度Moldtemperature80-90oC