PC+ABS-PC-510

台南市仁德區三甲里59-1號59-1,SanChia,JenTe,TainanCity71702,TaiwanTEL:886-6-266-5000FAX:[phone]~7WONDERLOY®PC-510PCalloy,non-halogenFlameRetardantPROPERTIESCONDITIONVALUEUNITMETHODPHYSICALSpecificGravity23℃1.17ISO2039MeltVolume-FlowRate260℃/2.16kg21cm3/10minISO1133Spiralflowlength260℃,2mmV:50%,P:50%45cmChimeimethodMoldShrinkage0.4~0.6%ISO2577RockwellHardness23℃R-113---ASTMD-785CLTEFlow:23-55℃8.00E-05cm/cm/℃ISO11359-2MECHANICALTensileStrength@Yield50mm/min55MpaISO527TensileStrength@break50mm/min45MpaISO527TensileElongation@Break50mm/min110%ISO527FlexuralStrength2mm/min80MpaISO178FlexuralModulus2mm/min2500MpaISO178IzodImpact（3.2mm）Notched,23℃45kJ/m2ISO180IzodImpact（3.2mm）Notched,-30℃15kJ/m2ISO180CharpyImpact（3.2mm）Notched,23℃45kJ/m2ISO179CharpyImpact（3.2mm）Notched,-30℃15kJ/m2ISO179THERMALHeatDistortionTemp.（unannealed）4mm,1.82Mpa120℃/hr73℃ISO75VicatSofteningTemp.（unannealed）1kg,50℃/hr5kg,50℃/hr9485℃ISO306ELECTRICALDielectricConstant1MHz3.1--IEC60250VolumeResistivity--3.9E+15Ohm*mIEC60093SurfaceResistivity--2.9E+15OhmIEC60093FLAMMABILITYFlameRating1.5mmV0UL-942.1mm5VBUL-943.0mm5VAUL-94台南市仁德區三甲里59-1號59-1,SanChia,JenTe,TainanCity71702,TaiwanTEL:886-6-266-5000FAX:[phone]~7PROCESSINGPARAMETERSDryingTemperature80℃DryingTime4HrsBarrelTemperature220~250℃MoldTemperature50~100℃Allfigureslistedhereisforreference,notguaranteed.Finalreviseddate：2014/6Unlessotherwisestatedtheresultsshowninthistestreportreferonlytothesample(s)tested.Thistestreportcannotbereproduced,exceptinfull,withoutpriorwrittenpermissionoftheCompany。Attentionisdrawntothelimitationofliability,indemnificationandjurisdictionissuesdefinedtherein.AnyholderofthisTestReportisadvisedthatinformationcontainedhereonreflectstheCompany’sfindingsatthetimeofitsinterventiononlyandwithinthelimitsofClient’sinstructions,ifany.TheCompany’ssoleresponsibilityistoitsClientandthisdocumentdoesnotexoneratepartiestoatransactionfromexercisingalltheirrightsandobligationsunderthetransactiondocuments.Anyunauthorizedalteration,forgeryorfalsificationofthecontentorappearanceofthisdocumentisunlawfulandoffendersmaybeprosecutedtothefullestextentofthelaw.