常见气体的粘度、密度值

.可编辑常见气体的粘度、密度值25℃，常压物质英文名密度kg/m3动力粘度μPa·s运动粘度mm2/s空气air1.16918.44815.787氨气ammonia0.69410.09314.539氩argon1.61322.62414.030丁烷butane2.4167.4063.065丁烯1-butene2.3278.1633.507二氧化碳carbondioxide1.78414.9328.369一氧化碳carbonmonoxide1.13017.64915.614二甲醚dimethylether1.8959.1004.801乙烷ethane1.2229.3547.654乙烯ethylene(ethane)1.13810.3189.066氢hydrogen0.0818.915109.69氢化硫hydrogensulfide1.38512.3878.942异丁烷isobutane2.4077.4983.115异丁烯isobutene2.3278.0853.474氪krypton3.38725.1327.419甲烷methane0.64811.06717.071氖neon0.81431.11338.239新戊烷neopentane3.0217.2592.403氮nitrogen1.13017.80515.753一氧化二氮nitrousoxide1.78514.8418.314氧oxygen1.29220.55015.910仲氢parahydrogen0.0818.915109.69丙烷propane1.8088.1464.507丙烯propylene1.7228.5604.971R115.74410.1621.769R1147.10910.8071.520R1156.34712.5151.972R1165.62614.1482.515R124.97111.8072.375R1245.65111.5932.051R1254.91512.9622.637R134.25214.3623.378R134a4.20111.8192.813.可编辑R143.56317.2444.839R142b4.16010.4212.505R143a3.44811.0873.215R152a2.72210.0813.704R2187.74812.4901.612R223.53912.6313.569R227ea7.05011.5911.644R232.84614.9135.240R236ea6.35410.8971.715R236fa6.33210.9601.731R245ca5.66110.1171.787R245fa5.63910.3031.827R322.12512.6135.937R411.38410.9557.913RC3188.31511.5051.384反丁烯二酸trans-2-butene2.3348.0283.440二氯碘甲烷trifluoroiodomethane8.08214.2771.767氙xenon5.32422.9844.317上一篇：不同介质的流量仪表选型应用下一篇：常见液体的粘度、密度值常见液体的粘度、密度值25℃，常压物质英文名密度kg/m3动力粘度μPa·s运动粘度mm2/s环己胺cyclohexane773.89884.691.143癸烷decane726.53848.101.167十二烷dodecane745.731358.81.822乙醇,酒精ethanol785.471084.91.381重水heavywater1104.51095.10.991庚烷heptane679.60388.480.572己烷hexane654.78296.280.452异己烷isohexane648.60272.800.421异戊烷isopentane614.98216.430.352甲醇methanol786.33543.710.691壬烷nonane714.09654.010.916辛烷octane698.27509.720.730戊烷pentane620.83217.900.351R1131563.2653.610.418.可编辑R1231463.9417.600.285R141b1233.8408.350.331R365mfc1257.1407.560.324甲苯toluene862.24556.250.645水water997.05890.080.893碳酸二甲酯dimethylcarbonate1061.5582.020.548碳酸二乙酯diethylcarbonate970.12751.90.775甲基叔丁醚methyltert-butylether734.91330.020.449上一篇：常见气体的粘度、密度值下一篇：常用材料密度表常用材料密度表材料名称密度(g/cm3)材料名称密度(g/cm3)煤油0.8水1.00玻璃2.60冰0.92铅11.30银10.50酒精0.79水银(汞)13.60汽油0.75灰口铸铁6.60-7.40软木0.25白口铸铁7.40-7.70锌7.10可锻铸铁7.20-7.40纯铜材8.90铜8.9059、62、65、68黄铜8.50铁7.8680、85、90黄铜8.70铸钢7.8096黄铜8.80工业纯铁7.8759-1、63-3铅黄铜8.50普通碳素钢7.8574-3铅黄铜8.70优质碳素钢7.8590-1锡黄铜8.80碳素工具钢7.8570-1锡黄铜8.54易切钢7.8560-1和62-1锡黄铜8.50锰钢7.8177-2铝黄铜8.6015CrA铬钢7.7467-2.5、66-6-3-2、60-1-1铝黄铜8.5020Cr、30Cr、40Cr铬钢7.82镍黄铜8.5038CrA铬钢7.80锰黄铜8.50铬、钒、镍、钼、锰、硅钢7.857-0.2、6.5-0.4、6.5-0.1、4-3锡青铜8.80纯铝2.705-5-5铸锡青铜8.80铬镍钨钢7.803-12-5铸锡青铜8.69铬钼铝钢7.65铸镁1.80.可编辑含钨9高速工具钢8.30工业纯钛（TA1、TA2、TA3）4.50含钨18高速工具钢8.70超硬铝2.850.5镉青铜8.90LT1特殊铝2.750.5铬青铜8.90工业纯镁1.7419-2铝青铜7.606-6-3铸锡青铜8.829-4、10-3-1.5铝青铜7.50硅黄铜、镍黄铜、铁黄铜8.5010-4-4铝青铜7.46纯镍、阳极镍、电真空镍8.85高强度合金钢`7.82镍铜、镍镁、镍硅合金8.85轴承钢7.81镍铬合金8.727铝青铜7.80锌锭（Zn0.1、Zn1、Zn2、Zn3）7.15铍青铜8.30铸锌6.863-1硅青铜8.474-1铸造锌铝合金6.901-3硅青铜8.604-0.5铸造锌铝合金6.751铍青铜8.80铅和铅锑合金11.371.5锰青铜8.80铅阳极板11.335锰青铜8.604-4-2.5锡青铜8.75金19.305铝青铜8.204-0.3、4-4-4锡青铜8.90变形镁MB11.76不锈钢0Cr13、1Cr13、2Cr13、3Cr13、4Cr13、Cr17Ni2、Cr18、9Cr18、Cr25、Cr287.75MB2、MB81.78Cr14、Cr177.70MB31.790Cr18Ni9、1Cr18Ni9、1Cr18Ni9Ti、2Cr18Ni97.85MB5、MB6、MB7、MB151.801Cr18Ni11Si4A1Ti7.52锻铝LD82.77不锈钢1Crl8NillNb、Cr23Ni187.90LD7、LD9、LD102.802Cr13Ni4Mn98.50钛合金TA4、TA5、TC64.453Cr13Ni7Si28.00TA64.40白铜B5、B19、B30、BMn40-1.58.90TA7、TC54.46BMn3-128.40TA84.56BZN15-208.60TB1、TB24.89BA16-1.58.70TC1、TC24.55BA113-38.50TC3、TC44.43锻铝LD2、LD302.70TC74.40LD42.65TC84.48LD52.75TC94.52防锈铝LF2、LF432.68TC104.53LF32.67硬铝LY1、LY2、LY4、LY62.76LF5、LF10、LF112.65LY32.73LF62.64LY7、LY8、LY10、LY11、LY142.80.可编辑LF212.73LY9、LY122.78LY16、LY172.84上一篇：常见液体的粘度、密度值下一篇：国产质量流量计基本参数目录简介方法分类分离方法1.气体扩散法2.电磁分离法3.热扩散法4.质量扩散法5.离心法6.精馏法7.化学交换法8.电解法9.光化学法参考书目展开简介方法分类分离方法1.气体扩散法2.电磁分离法3.热扩散法4.质量扩散法5.离心法6.精馏法7.化学交换法8.电解法9.光化学法参考书目展开编辑本段简介.可编辑同位素分离isotopeseparation同位素分离(一)将某元素的一种或多种同位素与该元素的其他同位素分离或富集的过程。同位素的发现依赖于同位素分离的实现。直至20世纪30年代初，同位素分离的目的主要是为了分析、研究元素的同位素组成。1931年发现重氢后，建立了重水生产工厂。在H.C.尤里提出同位素化学交换的理论后，建立了各种化学交换法分离同位素的装置。40年代以来，由于核工业的需要，同位素分离技术得以长足发展。铀235、重水、锂6、硼10以吨量级生产，并建立了大规模分离同位素过程的级联理论。碳13、氮15、氧18、硫34等以千克量生产，主要作示踪原子。编辑本段方法分类各种分离混合物的方法均可用来分离同位素，根据分离原理可以同位素分离(二)分为五大类：根据分离过程，各种方法可分类如下：对于统计的分离过程,单级分离系数α0偏离1的程度是衡量分离效率的标准。对于二元同位素混合物，要分离的同位素浓度为N（摩尔分数）,一次单元分离操作后分离为两部分（1和2）后，分离系数定义为：几种元素同位素的各种分离方法的α0值见表。同位素分离为使同位素有效分离，须将单级分离操作串联，以实现多级过程。为缩短平衡时间，降低能耗，建立了同位素分离的级联理论。编辑本段分离方法.可编辑气体扩散法又称孔膜扩散法。根据同位素分子通过孔膜（孔径约0.01～0.03微米）扩同位素分离(三)散速度的不同来分离同位素。结果，轻同位素富集在隔膜一侧，重组分富集在隔膜的另一侧。扩散法是分离铀235的主要方法，以六氟化铀为原料，分离系数α=1.0043,由几千个级组成级联以生产浓缩铀。（见铀同位素分离）电磁分离法它的工作原理与质谱法相类似。经第一次分离即可得到高富集的同位素，但产量很小，早期曾用于生产浓缩铀，后来主要用于生产克量级的重同位素，供科研使用。热扩散法当组成均匀的气体或液体混合物中有温度梯度时，轻组分将富集在热区而重组分将富集在冷区，这就是热扩散效应。热扩散法就是根据这一效应发展起来的。常用的装置为热扩散柱，其工作原理如图所示。将欲分离的同位素混合物放在两个垂直的同心圆管中间，内管加热，外壁冷却。由于热扩散效应，轻组分在热壁表面附近富集，重组分在冷壁表面富集，同时内壁附近气体受热上升，外管内壁附近气体因冷却下降。由于热对流的结果，富集了的轻组分气体和重组分气体经多次逆流接触，使得简单热扩散效应效果倍增。热扩散柱结构简单,操作方便,应用范围广泛，是实验室中分离轻同位素的主要手段。质量扩散法根据同位素混合物的不同组分在第三种气体（称为分离剂）中扩.可编辑同位素分离(四)散速度的不同来分离同位素。单级分离效率甚低。为得到高效分离，必须采用级联式质量扩散柱。此法适用于小规模的中等原子量元素的同位素分离。离心法根据质量不同的气体分子在离心场中的平衡分布不同来分离同位素。离心法的分离系数与绝对质量差有关,因此该法对分离重同位素（特别是铀235）有利。离心法单级分离系数高，最高可达1.5～2,因此,生产浓缩铀235需要级数少。台离心机处理物料量小，需要大量