聚合物乳液

1聚合物乳液关于聚合物乳液防水涂料的性能及应用研究摘要：防水涂料在我国建筑行业的投资成递增的趋势。并且近年来,我国防水涂料的研制取得很大的进步,并不断由溶剂型向乳液型和反应型,由低档向高弹性、高耐久性、功能性的方向发展，大力研究开发和推广高性能、高耐侯、环保型和多功能防水涂料,重点发展环保型聚氨脂、丙烯酸、橡胶改性沥青和水泥基渗透结晶型防水涂料。本文对聚合物乳液型防水涂料一一聚合物乳液建筑防水涂料与聚合物水泥防水涂料的性能及其应用进行了分析研究，探讨其防水机理、影响性能的因素及其合适使用场所关键词:聚合物乳液型防水涂料；性能；应用。2StudyofPerformanceandApplicationofPolymerEmulsionTypeWaterproofCoatingAbstract：Waterproofcoatinginourcountry,increasinginvestmentoftheconstructionindustryintoatrend.Andinrecentyears,thedevelopmentofwaterproofcoatinginChinahavemadegreatprogress,andconstantlyfromthesolventtotheemulsiontypeandreactiontype,fromlowtohighelasticity,highdurability,functionalityinthedirectionofthedevelopment,research,development,andvigorouslypromotehighperformance,highcorrosionresistance,environmentalprotectionandmulti-functionalwaterproofcoatings,focusingonenvironmentalprotectionpolyurethane,acrylic,rubbermodifiedasphaltandcement-basedpermeablecrystallizationtypewaterproofcoating.Studyofperformanceandapplicationofpolymeremulsiontypewaterproofcoating—polymeremulsionarchitecturalwatel’proofcoatingandpolymermodifiedcementitiouswaterproofcoatingdiscusstheirwarterprooitheory、factorsefectingonperformanceandtheirfitapplicationplace．KeyWords：polymeremulsiontypewaterpmofcoating；performance；application．1目录聚合物乳液.......................................................................................................................................1关于聚合物乳液防水涂料的性能及应用研究.......................................................................1StudyofPerformanceandApplicationofPolymerEmulsionTypeWaterproofCoating...............21.1引言.....................................................................................................................................21.2.产品的配方组成及生产工艺.....................................................................................2第二章探究.....................................................................................................................................22.1.产品性能的比较分析及防水机理的探讨.........................................................................22.1.1两种防水涂料性能的比较分析.............................................................................22.1.2两种产品防水机理的探讨.....................................................................................4第三章性能因素.............................................................................................................................53.1影响防水涂料性能的因素.................................................................................................53.1.1聚合物乳液性能及用量的影响.............................................................................53.1.2增塑剂的影响.........................................................................................................63.1.3颜填料量或聚灰比的影响.....................................................................................63.2其它因素的影响................................................................................................................7第四章应用.....................................................................................................................................84.1两种防水涂料的应用........................................................................................................84.2产品技术标准及应用.........................................................................................................8第五章环保.....................................................................................................................................95.1环保.....................................................................................................................................9第六章结语...................................................................................................................................106.1结语...................................................................................................................................102第一章前言1.1引言聚合物乳液型防水涂料分为不含水泥的单组份料浆型聚合物乳液建筑防水涂料及由以聚合物乳液为主的液料和含水泥的粉料组成的双组分复台型聚合物水泥防水涂料两种，在此不包括聚合物乳液改性沥青防水的涂料。该类产品作为一种新型水基(环保)防水涂料，以其有与混凝土、砂浆等基层粘结性好，对基层湿度要求低、无有毒溶剂挥发、透气性好、施工简便等的优势，随着我国房产、建筑业的迅猛发展及人们对环保要求的进一步提高，近几年从无到有到普及，得到了迅速发展和广泛应用1.2.产品的配方组成及生产工艺单组份聚合物乳液建筑防水涂料是由聚合物乳液(乙烯一醋酸乙烯共聚乳液、丙烯酸酯共聚乳液等)、增塑剂、助剂(包括分散剂、成膜助剂、消泡剂、防霉剂等)、填料、颜料(制成彩色)按适当配比在搅拌罐中以机械搅拌分散均匀的生产工艺制得的单组份粘稠料浆型防水涂料：聚合物水泥防水涂料是由液料与粉料两组份组成。液料由聚合物乳液(乙烯一醋酸乙烯共聚乳液、丙烯酸酯共聚乳液等)、增塑剂、助剂(成膜助剂、分散剂、消泡剂等)在搅拌罐中搅拌均匀后制得；粉料由水泥、石英砂、矿物粉、颜料粉(制成彩色)在于粉混合机中搅拌均匀后制得。使用时，将液料与粉料按一定配比机械搅拌成均匀料浆后即可施工。第二章探究2.1.产品性能的比较分析及防水机理的探讨2.1.1两种防水涂料性能的比较分析目前，两种聚合物乳液型防水涂料均已有建材行业标准颁布，其中JC／T8643—2000(聚合物乳液建筑防水涂料》于2001年1月1日实施，根据物理力学性能不同分为I类和Ⅱ类产品；JC／T894—2001《聚合物水泥防水涂料》于2002年6月1日实施，根据聚合物和水泥哪一种成分为主分为I型和Ⅱ型产品两种产品的行业标准性能要求(仅列出无处理时涂膜技术要求)见表1。表一两种聚合物乳液型建筑防水涂料的性能对比试验项目技术指标聚合物建筑防水涂料（单组份）聚合物建筑防水涂料（双组份）Ⅰ类Ⅱ类Ⅰ类Ⅱ类固体含量/%大于或等于65干燥时间表干时间/h小于或等于4实干时间/h小于或等于8拉伸强度（无处理）/MPa≥1.0≥1.5≥1.2≥1.8断裂伸长率（无处理）/%≥300≥300≥200≥80低温柔性（φ10mm棒）-10℃无裂纹-20℃无裂纹-10℃无裂纹——不透水性(0.3Mpa.30min)不透水潮湿基面粘结强度/MPa——≥0.5≥1.0抗渗性（背水面）/MPa————≥0.6从表1可看出，这两种产品大部分的性能指标均类似，最大的区别在于：单组份聚合物乳液建筑防水涂料具有较高的断裂延伸率和较好的低温柔性，而聚合物水泥防水涂料则具有相对较高的拉伸强度及与潮湿基面的粘结强度。这也正是这两种防水涂料使用场所有所区别并均得到广泛应用的原因所在。