POM-台湾台塑-FM090-物性表

FORMOCON® FM090聚甲醛（POM）共聚物FormosaPlasticsCorporationTechnicalData产品说明Characteristics:Standardflow,minimalmould Application:Buttonsandpressinfasteners,Plumbingandhardware,Gears,Electronicparts,Automotiveparts,Household,Bearing,Otherinjectionparts. AlsoknownasFORMOSACON总体材料状态•已商用：当前有效供货地区•北美洲•欧洲•亚太地区特性•良好的流动性用途•电气/电子应用领域•家用货品•纽扣•汽车领域的应用•轴承形式•粒子物理性能额定值(英制)额定值(公制)测试方法比重1.41 1.41g/cm³ASTMD792熔流率（熔体流动速率）(190°C/2.16kg)9.0g/10min9.0g/10minASTMD1238收缩率-流动(0.118in(3.00mm))0.018到0.022in/in1.8到2.2%ASTMD955吸水率(平衡,73°F(23°C),69%RH)0.22%0.22%ASTMD570机械性能额定值(英制)额定值(公制)测试方法抗张强度(屈服)8820psi60.8MPaASTMD638伸长率(断裂)60%60%ASTMD638弯曲模量370000psi2550MPaASTMD790弯曲强度13500psi93.2MPaASTMD790压缩强度ASTMD6951%应变4550psi31.4MPa10%应变15600psi108MPa冲击性能额定值(英制)额定值(公制)测试方法悬壁梁缺口冲击强度(73°F(23°C))1.2ft·lb/in64J/mASTMD256硬度额定值(英制)额定值(公制)测试方法洛氏硬度ASTMD785M级80 80 R级115 115 热性能额定值(英制)额定值(公制)测试方法载荷下热变形温度ASTMD64866psi(0.45MPa),未退火316°F158°C264psi(1.8MPa),未退火230°F110°C维卡软化温度324°F162°CASTMD1525熔融温度329°F165°CDSC线形热膨胀系数-流动4.7E-5in/in/°F8.5E-5cm/cm/°CASTMD696电气性能额定值(英制)额定值(公制)测试方法表面电阻率 41.0E+16ohm1.0E+16ohmASTMD257体积电阻率 4(73°F(23°C))1.0E+14ohm·cm1.0E+14ohm·cmASTMD257介电强度(0.0787in(2.00mm))610V/mil24kV/mmASTMD149如需购买请联系13825707544邱-RQQ1539078605FORMOCON® FM090聚甲醛（POM）共聚物FormosaPlasticsCorporation 电气性能额定值(英制)额定值(公制)测试方法介电常数IEC6025050Hz3.80 3.80 1kHz3.80 3.80 1MHz3.80 3.80 可燃性额定值(英制)额定值(公制)测试方法UL阻燃等级HB HB UL94如需购买请联系13825707544邱-RQQ1539078605