土木工程材料-硅酸盐水泥与普通水泥的技术性质

硅酸盐水泥与普通水泥的技术性质(一)细度筛分法:80um方孔筛,筛余不大于10.0%比表面积:300不合格品水50g100-105℃恒温,3g筛余3/50=6.0%阻力阻力越大越细kg/m2(二)凝结时间硅酸盐水泥普通水泥初凝:≮45min≮45min废品终凝:≯6.5hr≯10hr不合格品标准稠度用水量28±2mm(24%--30%)标准杆法：距底5-7mm距底3-5mm初凝进入0.5mm终凝(标养箱)(三)体积安定性(废品处理)体积安定性:f-CaO沸煮法f-MgO压蒸法(MgO≯5.0%)石膏过量长期浸水检查(SO3≯3.5%)试饼法(3h,无裂纹,无弯曲雷氏夹法检验(C-A≯5mm合格,否则不合格A张开后C(四)强度及强度等级水泥:标准砂1:3,w/c0.5,测强度强度等级硅42.5,52.5,62.5(六个,R)普32.5,42.5,52.5(六个,R)普通型,早强型(R型)二条3d,28d10040X40X100PC压板长40mm40x40PfFc=Pc/A=Pc/(40X40)(舍最大,最小)3fbLF5.1fR(五)含碱量Na2O+0.658K2O≯0.6%(或供需双方确定)(六)密度与堆积密度密度3.1--3.2,堆积密度900-1300(紧密1400-1700)某二种硅酸盐水泥,求强度等级.种类抗压破坏荷载(KN)抗折破坏荷载(KN)3d28d3d28dA33.3,34.234.5,33.633.8,34.268.7,69.269.5,70.167.3,68.11.801.821.762.832.752.79B37.2,37.838.9,39.240.1,39.283.1,83.783.3,84.794.5,82.21.901.601.772.512.903.12种类抗压破坏荷载(KN)抗折破坏荷载(KN)3d28d3d28dA33.3,34.234.5,33.633.8,34.268.7,69.269.5,70.167.3,68.11.801.821.762.832.752.79B37.2,37.838.9,39.240.1,39.283.1,83.783.3,84.794.5,82.21.901.601.772.512.903.12某二种硅酸盐水泥,求强度等级.种类抗压强度(MPa)抗折强度(MPa)强度等级3d28d3d28dA21.243.04.26.542.5B24.253.34.16.742.5R24.252.14.17.1标准17.042.53.56.542.522.042.54.06.542.5R六.水泥石的腐蚀与防止(一)水泥石的几种主要侵蚀作用1.软水侵蚀(溶出性侵蚀)(溶析)水流入水流出氢氧化钙浓度2.盐类侵蚀(1)硫酸盐侵蚀水中的钾钠氨的硫酸盐与水泥石中的Ca(OH)2起置换作用生成硫酸钙钙矾石(水泥杆菌)结晶二水石膏(膨胀)(2)镁盐侵蚀MgSO4+Ca(OH)2+2H2O=CaSO4·2H2O+Mg(OH)2MgCl2+Ca(OH)2=Mg(OH)2+CaCl2硫酸镁盐与硫酸盐双重侵蚀作用.无胶凝能力3.酸类侵蚀Ca(OH)2+CO2+H2O=CCO+2H2OCaCO3+CO2+H2OCa(HCO3)2溶出,Ca(OH)2浓度降低,加速2HCl+Ca(OH)2=CaCl+H2O(溶于水)H2SO4+Ca(OH)2=CaSO4·2H2O(硫酸盐腐蚀)4.强碱的腐蚀6NaOH+3CaO·Al2O3=3Na2O·Al2O3+3Ca(OH)22NaOH+CO2+H2O=Na2CO3+2H2O(结晶沉淀,膨胀)碳酸侵蚀铝酸钠,易溶(二)水泥石腐蚀的原因内因:–1.水泥石中存在易被腐蚀的组分Ca(OH)2和水化铝酸钙–2.水泥石本身不密实(有毛细孔,易进入)(三)防止措施–1.合理选用水泥品种–2.提高水泥的密实度–3.表面加保护层七.硅酸盐水泥和普通水泥的特性与应用(一)特性–1.凝结硬化快,强度高,尤其早期强度高.–2.抗冻性好.–3.水化热大.–4.不耐腐蚀.–5.不耐高温.(二)应用–1.适用重要结构的高强砼及预应力砼工程–2.适用于早强要求高的工程及冬季施工–3.适用于严寒地区遭受反复冻融及干湿交替的部位–4.不能用于海水和有侵蚀介质存在的工程–5.不能用于大体积砼–6.不能用于高温环境的工程