Q345B/C/D/E低合金高强度H型钢Q345B/C/D/E............低合金高强度H型钢化学成分表、化学成分的阐述及理论重量表。作者:康春波13752472226/022-585187621低合金高强度H型钢化学成分见表1。表1牌号等级CMnSiPSVNbTiAlCrNi≤≤≥≤Q295AB0.160.80~1.500.550.0450.0400.0450.0400.02~0.150.015~0.0600.02~0.20------Q345ABC0.201.00~1.600.0450.0400.0350.0300.0250.0450.0400.0350.0300.025--0.0150.0150.015----------DE0.18Q390ABCDE0.200.0450.0400.0350.0300.0250.0450.0400.0350.0300.0250.02~0.20--0.0150.0150.0150.300.70Q420ABCDE0.201.00~1.700.0450.0400.0350.0300.0250.0450.0400.0350.0300.025--0.0150.0150.0150.40Q460CDE0.200.0350.0300.0250.0350.0300.0250.0150.70注:①表中的Al为全铝含量。如化验酸溶铝时,其含量应不小于0.010%。②Q295级钢的C含量到0.18%也可交货;不加V,Nb,Ti的Q295级钢,当C≤0.12%时,Mn含量上限可提高到1.80%。③Q345级钢的Mn含量上限可提高到1.70%;厚度≤6mm的钢板和钢带与厚度≤16mm的热连扎钢板、钢带的Mn含量下限可降低0.20%。④型钢和棒钢的Nb含量下限为0.005%;各牌号的Cr,Ni,Cu残余元素的含量都不大于0.30%,供方如能保证,可不做分析。⑤为改善钢的性能,Q390,Q420,Q460级钢可加入少量Mo元素,各牌号钢还可加入RE元素,其加入量控制在0.02%~0.20%。⑥经供需双方协商,Q420级钢可加入N元素,其熔炼分析含量为0.010%~0.020%。⑦供应商品钢锭,连铸坯时,为保证钢的力学性能符合标准规定,其C和Si元素的含量下限可根据需方要求另行协议。⑧在保证钢材力学性能符合要求的情况下,用Nb作为细化晶粒元素时,Q345和Q390钢的Mn含量下限可低于表中的下限含量。⑨除各牌号A,B级钢外,钢中的细化晶粒元素(V,Nb,Ti,Al)应至少含有其中的一种,如这些元素同时使用,则至少应有一种元素的含量不低于规定的最小值。⑩为改善钢的性能,各牌号A,B级钢壳加入V、Nb或Ti等细化晶粒元素,其含量应符合表中规定;如不作为合金元素加入时,其下限不受限制。⑪当钢中不加入细化晶粒元素时,不进行该元素含量的分析,也不予保证。⑫A级钢或B级钢允许同一牌号、同一质量等级、同一冶炼和浇注方法、不同炉罐号组成混合批。但每批不得多于6个炉罐号,且各炉罐C含量之差不得大于0.02%,Mn含量之差不得大于0.15%。2低合金高强度H型钢的截面尺寸和理论重量见表2。H—高度;B—宽度;t1—腹板厚度;t2—翼缘厚度;截面尺寸/mm国标理论重量/(kg/m)HBt1t21001006817.21251256.5923.81481006921.4150755714.315015071031.9175905818.21751757.51140.31941506931.2198994.5718.52001005.5821.720020081250.5200204121256.724417571144.12481245825.82501256929.725025091472.4250255141482.229420081257.32943021212852981495.5832.629820191465.93001506.5937.3300300101594.5300305151510634025091479.734434810161153461746941.835017571150350350121913738840215151413903001016107394398111814739619971156.74002008136640015081355.840040013211724144051828233414202102094.5440300111812444619981266.745020091476.54823001115115488300111812949619991479.5500200101689.65062011119103582300121713758830012201515943021423175596199101595.160020011171066003041626198606201122012069230013201667003001324185792300142219180030014262109003001628243H型钢的重量根据需方的要求可以理论计算也可以过磅计算。
本文标题:Q345BCDE低合金高强度H型钢
链接地址:https://www.777doc.com/doc-2854056 .html