膨胀聚苯板薄抹灰,胶粉聚苯颗粒外墙外保温系统施工及验收技术导则

膨胀聚苯板薄抹灰、胶粉聚苯颗粒外墙外保温系统施工及验收技术导则（试行）聚氨酯保温管沈阳堵漏防水辽宁不锈钢沈阳304不锈钢板天津304不锈钢板沈阳代办工商营业执照湖南省建设厅二○○六年三月·长沙目录1总则··················································································12基本规定············································································32.1材料选择····································································32.2系统工程性能······························································32.3系统及系统组成材料性能指标要求···································43施工··················································································73.1一般规定····································································73.2膨胀聚苯板薄抹灰外墙外保温系统···································93.3胶粉聚苯颗粒外墙外保温系统·······································114验收················································································124.1一般规定··································································124.2膨胀聚苯板薄抹灰外墙外保温系统·································154.3胶粉聚苯颗粒外墙外保温系统·······································17附表A外墙外保温系统工程材料现场抽样复检项目······················19附表B外墙外保温系统隐蔽工程施工质量验收记录······················21附表C外墙外保温系统检验批质量验收记录·······························22附表D外墙外保温系统分项工程质量验收记录····························23附表E外墙外保温系统子分部工程质量验收记录·························24附录A外墙外保温系统检测试验方法········································2511总则1.0.1为规范膨胀聚苯（EPS）板薄抹灰外墙外保温系统（以下简称膨胀聚苯板薄抹灰系统）、胶粉聚苯颗粒外墙外保温系统（以下简称胶粉聚苯颗粒系统）工程施工及验收行为，保证工程质量，做到技术先进、安全可靠、经济合理，减少建筑能耗，满足建筑节能要求，特制定本导则。1.0.2本导则适用于新建民用建筑的混凝土和砌体结构采用膨胀聚苯板薄抹灰系统和胶粉聚苯颗粒系统的工程施工及验收。1.0.3此两种外墙外保温系统工程的施工和验收除应符合本导则要求外，尚应符合国家现行有关强制性标准的规定。膨胀聚苯板薄抹灰系统和胶粉聚苯颗粒系统在行业标准《外墙外保温工程技术规程》（JGJ144－2004）中分别称为“EPS板薄抹灰外墙外保温系统”和“胶粉聚苯颗粒外墙外保温系统”。1.0.4系统的各种组成材料均应由系统产品制造商配套供应，且其膨胀聚苯板必须为阻燃型。系统产品制造商必须提供相应鉴定证书及全套型式检验报告。1.0.5膨胀聚苯板薄抹灰外墙外保温系统的国家标准（JG149－2003）中规定其饰面层为涂料，尚未有以面砖作饰面层的相应国家、行业标准及图集。因此，我省现阶段一般不应在膨胀聚苯板薄抹灰外墙外保温系统中采用面砖作其饰面。1.0.6胶粉聚苯颗粒系统一般不宜采用面砖饰面。如采用面砖饰面，必须严格按照有关国家行业标准及图集规定施工及验收，除必须具有型式检验报告外，还必须按规定提供其在设防裂度或以上等级地震作用下的抗震试验验证报告。1.0.7挤出聚苯板（或称挤塑板，XPS）薄抹灰外墙外保温系统尚无相应的国家、行业标准及图集，因此，我省现阶段一般不应采用挤出2聚苯板（XPS）薄抹灰外墙外保温系统。1.0.8对以上没有国家、行业标准及省级以上建设行政主管部门批准的图集的建筑节能技术在工程中应用，必须严格按照《建设工程勘察设计管理条例》（国务院令第293号）的要求，由国家认可的检测机构进行试验、论证，出具检测报告，并经国务院有关部门或省级建设行政主管部门组织专家技术委员会审定后方可采用。32基本规定2.1材料选择2.1.1所用材料的品种、规格应符合设计要求，其性能应符合国家、行业和本省现行的有关标准要求。各组成部分应具有物理、化学稳定性。所有组成材料应彼此相容并应具有防腐性。在可能受到生物侵害（鼠害、虫害等）时，还应具有防生物侵害性能。2.1.2采用的产品应具有产品合格证、相应性能的出厂检验报告和有相应资质的检测机构的型式检验报告。进口产品尚应按规定提供商品检验报告。应选用经省及以上相关部门组织技术鉴定并推广应用的建筑节能技术和产品。严禁采用国家或湖南省建设行政主管部门明令淘汰的建筑材料和产品。2.2系统工程性能2.2.1应能长期承受自重而不产生有害的变形。2.2.2应能承受风荷载的作用而不产生破坏。2.2.3应能耐受室外气候的长期反复作用而不产生破坏。2.2.4在罕遇地震发生时不应从基层上脱落。2.2.5高层建筑工程中还应具有防火构造措施。2.2.6应具有防水渗透性能。2.2.7应能适应基层的正常变形而不产生裂缝或空鼓。2.2.8外保温复合墙体的保温、隔热和防潮性能应符合国家现行标准《民用建筑热工设计规范》GB50176、《夏热冬冷地区居住建筑节能设计标准》JGJ134、《外墙外保温工程技术规程》JGJ144、《公共建筑节能设计标准》GB50189及《湖南省居住建筑节能设计标准》4DBJ43/001－2004。同时，亦应符合《膨胀聚苯板薄抹灰外墙外保温系统》JG149－2003及《胶粉聚苯颗粒外墙外保温系统》JG158－2004。2.2.9在正确使用和正常维护的条件下，使用年限不应少于25年。2.3系统及系统组成材料性能指标要求2.3.1应按有关规定对外墙外保温系统进行耐候性检验。经耐候性试验后，不得出现饰面层起泡或剥落、保护层空鼓或脱落等破坏，不得产生渗水裂缝。抹面层与保温层的拉伸粘结强度不得小于0.1MPa，并且破坏部位应位于保温层内。2.3.2应按有关规定对胶粉聚苯颗粒外墙外保温系统进行抗拉强度检验，抗拉强度不得小于0.1MPa，并且破坏部位不得位于各层界面。2.3.3应按有关规定对胶粘剂进行拉伸粘结强度检验。胶粘剂与水泥砂浆的拉伸粘结强度在干燥状态下不得小于0.6MPa，浸水48h后不得小于0.4MPa；与膨胀聚苯板的拉伸粘结强度在干燥状态和浸水48h后均不得小于0.1MPa，并且破坏部位应位于膨胀聚苯板内。2.3.4应按有关规定对玻纤网进行耐碱拉伸断裂强力检验。玻纤网经向和纬向耐碱拉伸断裂强力均不得小于750N/50mm，耐碱拉伸断裂强力保留率均不得小于50%。2.3.5其他性能应符合表2.3.5规定。2.3.6其他主要组成材料性能应符合表2.3.6规定。2.3.7外墙外保温系统型式检验报告有效期为2年。5表2.3.5外墙外保温系统性能要求检验项目性能要求抗风荷载性能系统抗风压值Rd不小于风荷载设计值。安全系数K应不小于1.5抗冲击性建筑物首层墙面以及窗口等易受碰撞部位：10J级；建筑物二层及二层以上墙面等不易受碰撞部位：3J级吸水量胶粉聚苯颗粒外墙外保温系统：浸水1h，吸水量≤1000g/㎡。试验方法见JG158-2004。膨胀聚苯板薄抹灰外墙外保温系统：浸水24h,吸水量≤500g/㎡。试验方法见JG149-2003。耐冻融性能30次冻融循环后，保护层无空鼓、脱落，无渗水裂缝；保护层与保温层的拉伸粘结强度不小于0.1MPa，破坏部位应位于保温层。水中浸泡24h，只带有抹面层和带有全部保护层的系统的吸水量均小于0.5kg/m2时，不检验耐冻融性能。热阻复合墙体热阻符合设计要求。试验方法见JGJ144－2004附录A第A·9节。不透水性试样防护层内侧无水渗透。试验方法分别见JG158－2004、JG149－2003。水蒸气湿流密度g/cm2·h≥0.85试验方法分别见JG158－2004、JG149－2003。饰面砖粘贴强度（T型）/MPa（现场抽测）≥0.4试验方法见JG158－2004抗震性能（T型）设防烈度等级下，面砖饰面及保温系统无脱落。6表2.3.6外墙外保温系统组成材料性能要求检验项目性能要求试验方法膨胀聚苯板胶粉聚苯颗粒保温材料密度（kg/m3）18～22——GB/T6343-1995干密度（kg/m3）——180～250GB/T6343-1995(70°C衡重)导热系数[W/（m·K）]≤0.041≤0.060GB/T10294-1988水蒸气湿流密度g/cm2·h≥0.85≥0.85分别见JG149-2003JG158-2004压缩性能（MPa）（形变10%）≥0.10≥0.25（养护28d）GB8813-1988抗拉强度（MPa）干燥状态≥0.10≥0.10JGJ144-2004附录A第A.7节浸水48h，取出后干燥7d——线性收缩率（%）——≤0.3GBJ82-1985尺寸稳定性（%）≤0.3——GB8811-1988软化系数——≥0.5（养护28d）JGJ51-2002燃烧性能阻燃型——GB/T10801.1-2002燃烧性能级别——B1GB8624-1997抹面胶浆、抗裂砂浆、界面砂浆与膨胀聚苯板或胶粉聚苯颗粒拉伸粘结强度（MPa）干燥状态和浸水48h后≥0.10，破坏界面应位于膨胀聚苯板或胶粉聚苯颗粒JGJ144-2004附录A第A.8节饰面材料必须与其他系统组成材料相容，应符合设计要求和相关标准规定锚栓符合设计要求和相关标准规定73施工3.1一般规定3.1.1施工单位应具备装饰装修专业资质或施工总承包资质，施工现场质量管理应有相应的施工技术标准、健全的质量管理体系、施工质量控制和检验制度。3.1.2除原设计单位或具有相应资质的设计单位外，任何单位和个人不得擅自修改设计文件。施工单位应认真研阅设计文件，若发现问题，应与建设单位和设计单位洽商。如需办理设计变更和审查，应遵照相关规定办理，重大设计变更须经有关部门审批同意。3.1.3施工时，任何单位和个人不得擅自更改设计时选用的外保温系统构造和材料。3.1.4施工单位应根据设计要求编制施工技术方案，对施工人员应进行技术交底和专业技术培训。并应按相关的施工技术标准对施工过程实行质量控制。3.1.5外保温工程的防水处理。施工前应具有外保温工程的密封和防水构造设计，确保水不会渗入保温层及基层，重要部位应有详图。水平或倾斜的出挑部位以及延伸至地面以下的部位应做防水处理。在外保温系统上安装的设备或管道应固定于基层上，并应做密封和防水设计。外墙上的任何附着件不应损害保温层的整体性，对连接部位应做保温和防水处理。3.1.6主体结构的支模架洞孔等应修补完成后再做外保温，不得用保温材料填嵌。3.1.7施工前，外门窗洞口应通过验收，洞口尺寸、位置应符合设计8要求和质量要求，门窗框或辅框应安装完毕。窗口外侧四周墙面应按设计要求进行保温处理。3.1.8外墙出挑构件及附墙部件，如：阳台、雨罩、靠外墙阳台拦板、