碳钢铸件锻件满足NACE不要做HIC-SSC试验

 碳钢阀门铸件和锻件如何满足NACE要求How to make NACE material with carbon steel casting and forging:  By JYS  铸件锻件没有必要做HIC、SSC试验  NACE MR0175 ISO 15156 2 part 2 （2009）: Carbon and low alloy steel  NACE requirement 8EvaluationofcarbonandlowalloysteelsfortheirresistancetoHIC/SWC TheequipmentusershallconsiderHIC/SWCasdefinedinANSI/NACEMR0175/ISO15156-1whenevaluatingflat-rolledcarbonsteelproductsforsourserviceenvironmentscontainingeventraceamountsofH2SandshallconsiderHIC/SWCtestingoftheseproducts.AnnexBprovidesguidanceontestmethodsandacceptancecriteriatoevaluateresistancetoHIC/SWC.对于用钢板卷制的压力容器在含H2S介质时，必须进行HIC/SWC试验………….TheprobabilityofHIC/SWCisinfluencedbysteelchemistryandmanufacturingroute.Thelevelofsulfurinthesteelisofparticularimportance,typicalmaximumacceptablelevelsforflat-rolledandseamlessproductsare0.003%massfractionand0.01%massfraction,respectively.Conventionalforgingswithsulfurlevelslessthan0.025%massfraction,andcastings,arenotnormallyconsideredsensitivetoHICorSOHIC.HIC/SWC受化学成份和制造过程影响。硫含量是特别重要的，通常认为对于钢板制品硫含量不大于0.003%，无缝钢管硫含量不大于0.1%，锻件硫含量不大于0.025%，铸件没有限制，上列情况下，材料对HIC（SOHIC）不敏感 A.2SSC-resistantcarbonandlow-alloysteelsandtheuseofcastironsCarbonandlow-alloysteels,productsandcomponentsthatcomplywithClauseA.2are,withstatedexceptions,qualifiedinaccordancewiththispartofANSI/NACEMR0175/ISO15156withoutfurtherSSCtesting.碳钢和低合金钢，在下列情形下不用做SSC试验：A.2.1.2Parentmetalcomposition,heattreatmentandhardnessCarbonandlowalloysteelsareacceptableat22HRCmaximumhardnessprovidedtheycontainlessthan1%nickel,arenotfree-machiningsteelsandareusedinoneofthefollowingheat-treatmentconditions:碳钢和低合金钢在以下情形下不用做SSC试验a)hot-rolled(carbonsteelsonly);热轧碳钢（不含低合金钢）b)annealed;退火态c)normalized正火态d)normalizedandtempered;正火+回火e)normalized,austenitized,quenched,andtempered;正火+淬火+回火f)austenitized,quenched,andtempered.淬火+回火A.2.1.3Carbonsteelsacceptablewithrevisedoradditionalrestrictions………….a)ForgingsproducedinaccordancewithASTMA105areacceptableifthehardnessdoesnotexceed187HBW.A105锻件硬度不大于HB187b)b)WroughtpipefittingstoASTMA234,gradesWPBandWPCareacceptableifthehardnessdoesnotexceed197HBW.7.2.1.4SSCregions1,2and3IntheabsenceofsuitablechoicesfromAnnexA,carbonandlow-alloysteelsmaybetestedandqualifiedforuseunderspecificsour-serviceconditionsorforusethroughoutagivenSSCregion7.2.2SOHICandSZCTheusershouldconsiderSOHICandSZC,asdefinedinANSI/NACEMR0175/ISO15156-1,whenevaluatingcarbonsteelsinplateformandtheirweldedproductsforsourserviceinH2S-containingenvironments.通常锻件铸件都满足上述要求，即锻件硫含量不大于0.025%，锻件、铸件都进行正火、退火或调质热处理。所以锻件做件不用做HIC、SSC试验。锻件铸件是否要控制S/P杂质元素含量：在NACE标准要求中，仅提出锻件硫含量不大于0.025%，没有其它限制。但不同公司要求各异，甚至提出低硫磷要求：TOTAL：forgingP≤0.020,S≤0.015;castingP/S≤0.020Worleyparsons:forgingP ≤0.030,S≤0.025;castingP≤0.030,S≤0.035也有要求低硫磷，P/S≤0.015%………硫、磷等杂质元素对材料的负面影响是多重的，使材料变脆，降低冲击韧性，增加铸造、锻造或焊接等制造过程中的开裂倾向。尽管NACE没有严格的要求，但尽量降低S，P，O,，H等杂质含量还是有益的。综合国内外对NACE的各种内控标准，建议控制如下：1.锻件：将S/P控制P/S≤0.020%，要求精炼，脱气钢a.因为中国大量生产并出口优质钢管，国内市场满足ASTMA105标准的优质钢已普遍。选用精炼脱气的优质钢做锻件，降低S/P含量，也可减少钢材中O、H等杂质元素。按照这个要求控制，也可抑制锻造厂使用劣质的“地条钢”b.确保锻造比超过3:1：钢锭或连铸坯中的缩松、粗大晶粒、化学偏析，可能通过锻造消除，但锻造比小，则上列缺陷会遗传到锻件中。2.铸件：将S/P控制P/S≤0.025%国内阀门铸件以中频感应炉为主，少量铸造厂有电弧炉。电弧炉脱氧还原过程能有效降低钢中的S/P等杂质元素；但中频感应炉较困难，铸造厂应按下列控制：a.优质废钢，对废钢化验，确认S/P很低，选用钢板冲边，钢管退头等。废钢不应有锈、水、油、漆、镀锌等。b.采用中低碳锰铁，减少加入合金材料时增S/Pc.采用镁砂做炉衬材料和钢包内衬d.用铝块（棒）做炉内和包内脱氧