JBT 10737-2007 内燃机 粉末冶金气门座技术条件气门座技术条件(TLG)

ICS27.020J93中华人民共和国机械行业标准JB/T10737-2007内燃机粉末冶金气门座技术条件Internalcombustionengines—Powdermetallurgyvalveseatinsets—Specification(讨论稿)2007-05-29发布2007-11-01实施中华人民共和国国家发展和改革委员会发布()JB/T10737－2007目次前言························································································································Ⅱ1范围············································································································12规范性引用文件····································································································13术语和定义···········································································································14技术要求············································································································25检验方法············································································································36检验规则············································································································37标志、包装、贮存········································································································3IⅠ()JB/T10737－2007前言内燃机的气门座是保持燃烧室密封性、将气门热量传递到气缸盖，并保证内燃机可靠工作的一个重要零件。随着汽车工业的发展，性能指标的日趋强化，特别是实施日益严格的环保法规要求汽油无铅化，使气门座处于日益严酷的热力、化学和机械力综合作用的状况下工作，为了保证其工作可靠性和使用寿命，因而对所选用材料的性能指标提出了更高的要求。采用已有的普通材料制造的气门座，已很难适应发动机高比功率的强化要求。粉末冶金材料由于具有优良的耐热性和耐磨性、耐腐蚀性、切削量小、材料利用率高、合金配比和零件设计自由度大、生产成本低等优点，因而在内燃机气门座领域得到越来越广泛的应用。由于国内目前尚未制定粉末冶金气门座的技术标准，为了促进技术进步和粉末冶金气门座产品共性的质量指标有一个评定依据，参照国外先进工业国家企业技术文件和产品图样，特制定本标准。本标准由中国机械工业联合会提出。本标准由全国内燃机标准化技术委员会提出并归口。本标准由上海内燃机研究所负责起草。本标准起草单位：上海内燃机研究所、安庆帝伯粉末冶金有限公司、绵阳沃特尔粉末冶金有限公司本标准主要起草人：本标准于2007年5月29日首次发布。IIJB/T10737－2007内燃机粉末冶金气门座技术条件1范围本标准规定了内燃机粉末冶金气门座的技术要求、检验方法、检验规则和标志、包装、运输、贮存。本标准适用于气缸直径200mm以下的往复活塞式内燃机的镶块式粉末冶金气门座（以下简称粉末冶金气门座）。2规范性引用文件下列文件中的条款通过本标准的引用而成为本标准的条款。凡是注日期的引用文件，其随后所有的修改单（不包括勘误的内容）或修订版均不适用于本标准，然而，鼓励根据本标准达成协议的各方研究是否可使用这些文件的最新版本，凡是不注日期的引用文件，其最新版本适用于本标准。GB/T223(所有部分)钢铁及合金化学分析方法GB/T1184公差未注公差值（GB/T1184-1996,eqvISO2768-2：1989）GB/T1958形状和位置公差检测规定GB/T2828.1计数抽样检验程序第1部分：按接收质量限（AQL）检索的逐批检验抽样计划（ISO2859-1：1999）GB/T5163可渗性烧结金属材料密度的测定GB/T6804烧结金属衬套径向压溃强度的检测方法GB/T9097.1烧结金属材料（不包括硬质合金）表观硬度的检测第一部分：截面硬度基本均匀的材料JB/T2798铁基粉末冶金烧结制品金相标准JB/T8063.1～8063.3粉末冶金材料与制品化学分析方法3术语和定义下列术语和定义适用于本标准。①②④⑦⑤⑨⑥⑧③⑩⑿图13.1外径externaldiameter外圆柱面的直径（见图1①）。3.2内径interiordiameter内孔面最小处的直径（见图1②）。JB/T10737－20073.3密封面大径airproofsurfacediameter与气门盘锥面接触的圆锥面与密封端面相交圆的直径（见图1③）。3.4高度height密封端面与底座面的距离（见图1④）。3.5压入倒角深度presschamferangledepth压入导向角与外圆柱面相交处至底座面的轴向距离（见图1⑤）。3.6压入倒角宽度chamferanglebreadth压入导向角与底座面交处至外圆柱面的径向距离（见图1⑥）。3.7上层材高度superstratummaterialheight采用双层材料时靠近密封端面一侧材料的高度（见图1⑦）。3.8外圆柱面externalcylinder粉末冶金气门座与气缸盖接触的圆柱面（见图1⑧）。3.9上端面airproofsurface粉末冶金气门座与气门盘锥面接触一侧的端面（见图1⑨）。3.10底座面foundationsurface粉末冶金气门座与气缸盖接触端面（见图1⑩）。3.11内圆面interiorcylinder粉末冶金气门座内孔面（见图1○11）。3.12压入角度presschamferangle粉末冶金气门座压入角度（见图1⑿）。4技术要求4.1总则粉末冶金气门座应符合经规定程序评审批准的产品图样及技术文件规定，亦可按本标准的规定制造。4.2材料4.2.1推荐采用材料的化学成分应符合表1的规定。4.2.2推荐采用材料的物理、力学性能应符合表2的规定。4.2.3根据需要，允许选用能满足本标准技术要求和使用要求的其他材料。4.3金相组织采用表1所列推荐材料生产的粉末冶金气门座的金相显微组织应为珠光体、铁素体、游离石墨和合金强化相。珠光体+强化相含量不低于80%，不得有网状渗碳体，游离渗碳体不得大于5%，不得有夹杂物、孔洞及裂纹；采用其他材料生产的粉末冶金气门座其金相显微组织应符合经规定程序批准的产品图样和技术文件之规定。12JB/T10737－20074.4尺寸公差粉末冶金气门座尺寸公差值不得大于表3规定。表1类别FQZ1FQZ2FQZ3FQZ4FQZ5Fe余量余量余量余量余量C化合0.7～1.20.9～1.40.9～1.40.7～1.50.9～1.2Cu1.0～3.0-0.4～0.610.0～20.012.9～21.3Mo0.3～1.02.0～5.06.0～8.04.5～9.57.6～15.0P0.1～0.3———-Ni0.1～0.31.0～2.51.9～3.61.0～2.42.6以下Cr—3.0～5.03.2～5.35.2～9.53.7～7.7Co—5.0～8.55.0～7.05.3～9.03.3～7.5W————2.4～4.1V————0.3～1.75化学成分（%）其余≤1.0≤1.0≤1.0≤1.0≤4.0密度（g/cm3）6.95～7.206.5～6.96.5～6.97.5～8.0单7.5～8.1双7.3～7.8单7.3以上双硬度（HRB/HRC）HRB80～100HRB80～100HRB85～100HRC40～50HRC35～50用途汽油机进气门座汽油机排气门座汽油机排气门座柴油机进、排气门座燃气发动机进、排气门座备注单层材双层材单、双层材下层材单、双层材表2项目密度（g/cm3）硬度（密封面）径向压溃强度系数k值（kgf/mm2）指标≥6.5（双层材为整体密度）,系指整体干密度（不含油）。75HRB～110HRB或25HRC～50HRC，同一片粉末冶金气门座上各点硬度差不得大于10个HRB单位或6个HRC单位。≥40表3mm粉末冶金气门座部位外圆直径内圆直径高度压入角宽度压入角深度密封面直径尺寸公差值≤0.026≤0.30≤0.05≤0.2≤0.3≤0.44.5表面粗糙度粉末冶金气门座的表面粗糙度Ra值应符合表4规定。表4μm粉末冶金气门座部位外圆柱面内孔面上下端面压入角表面粗糙度Ra值≤0.8≤3.2≤1.6≤1.64.6形状和位置公差粉末冶金气门座的形状和位置公差按GB/T1184规定的如下等级制造：a）外圆柱面对底座面的垂直度为7级；b）密封端面对底座面的平行度为7级；JB/T10737－2007c）内圆柱面对外圆柱面的同轴度为9级；d）外园的圆柱度为8级。4.7装配过盈量粉末冶金气门座的常温装配过盈量推荐值：与铸铁气缸盖相配为粉末冶金气门座外径的0.0015～0.003；与铝气缸盖相配为粉末冶金气门座外径的0.002～0.0035。4.8外观粉末冶金气门座的表面不得有裂纹、碰伤、孔洞、毛刺及锈蚀等缺陷，不得有磨削产生的擦伤、波浪纹、塌边等缺陷。4.9使用寿命粉末冶金气门座的寿命应不低于内燃机大修期。用户在正常使用情况下，粉末冶金气门座圈应与发动机保持同等寿命。5检验方法5.1材料粉末冶金气门座用材料的化学成分按JB/T8063.1～JB/T8063.3和GB/T223中的规定进行分析和检测。5.2硬度使用洛氏硬度计按GB/T9097.1中的规定进行检测，单层材料检测底座面硬度，双层材料分别检测底座面和密封端面硬度。：5.3表面粗糙度使用表面粗糙度仪进行检测。：5.4外径使用外径千分尺或专用检具检测X、Y两个垂直方向径向尺寸，以千分尺测定结果为准。5.5密封面直径使用工具显微镜或投影仪检测。5.6压入倒角深度、宽度及角度使用轮廓仪检测压入倒角深度、宽度及角度，或用工具显微镜检测压入倒角深度、宽度。5.7材料密度按GB/T5163的规定进行检测。5.8径向压溃强度系数（K值）按GB6804的规定进行检测。5.9显微组织用金相显微鏡按JB/T2798的规定或企业标准进行检测。5.10形状和位置公差按GB/T1958的规定进行检测。5.11外观使用标准样块或图示进行目视检查。6检验规则6.1每个产品须经制造厂技术检验部门检验合格后方能出厂。6.2需方抽查产品质量时，应按GB/T2828.1的规定抽检，检验项目、组批原则、抽样方案、判定与复验规则按制造厂与客户商定的技术文件。6.3国家主管部门抽查产品质量时，按主管部门批准的实施细则的规定。7标志、包装、运输和贮存3JB/T10737－20077.1标志7.1.1包装盒上应标明：a）制造厂名称、商标及地址；b）产品名称、材料、型号及零件号；c）数量；d）产品质量等级；e）包装日期及防锈有效期；f）执行标准号。7.1.2包装箱外部应标明：a）商标分类图示标志；b）制造厂名称、商标及地址；c）产品名称、材料及型号；d）数量；e）总质量及外形尺寸；f）收货单位及地址；