塑料模具设计说明书

1湖南工学院课程设计设计课题注塑模具设计设计学院机械工程学院设计班级成型1001班设计者姓名原育民设计时间2013年12月2目录1.塑件的工艺分析....................................................................................41.1塑件的成型工艺性分析.................................................................41.1.1塑件材料ABS的使用性能.................................................51.1.2塑件材料ABS的加工特性.................................................51.2塑件的成型工艺参数确定............................................................62模具的基本结构及模架选择.................................................................62.1模具的基本结构............................................................................62.1.1确定成型方法.......................................................................62.1.2型腔布置...............................................................................72.1.3确定分型面...........................................................................72.1.4选择浇注系统.......................................................................82.1.5确定推出方式.......................................................................82.1.6侧向抽芯机构.......................................................................92.1.7选择成型设备........................................................................92.2选择模架......................................................................................112.2.1模架的结构.........................................................................112.2.2模架安装尺寸校核.............................................................113模具结构、尺寸的设计计算...............................................................123.1模具结构设计计算......................................................................123.1.1型腔结构.............................................................................123.1.2型芯结构.............................................................................1233.1.3斜导柱、滑块结构.............................................................123.1.4模具的导向结构.................................................................123.2模具成型尺寸设计计算..............................................................133.2.1型腔径向尺寸.....................................................................123.2.2型腔深度尺寸.....................................................................133.2.3型芯径向尺寸.....................................................................133.2.4型芯高度尺寸.....................................................................143.3模具加热、冷却系统的计算......................................................153.3.1模具加热.............................................................................153.3.2模具冷却.............................................................................154.模具主要零件图及加工工艺规程......................................................154.1模具定模板零件图及加工工艺规程....................................154.2模具侧滑块零件图及加工工艺规程.......错误!未定义书签。4.3模具动模板（型芯固定板）零件图及加工工艺规程........165模具总装图及模具的装配、试模..........................错误!未定义书签。5.1模具的安装试模.....................................................................175.2.试模前的准备.......................................................................175.3模具的安装及调试.................................................................205.4试模........................................................................................215.5检验.........................................................................................216.排气系统的设计...................................................................................227.参考文献..............................................................................................224塑料注射模具设计与制造实例通过一个典型的塑料制品，介绍了从塑件成型工艺分析到确定模具的主要结构，最后绘制出模具图的塑料注射模具设计全过程。1.塑件的工艺分析1.1塑件的成型工艺性分析塑件图产品材料：ABS塑件尺寸：如图所示塑件要求：1.件壁厚均匀，不允许有裂纹和变形缺陷。2.脱模斜度30‘~1，3.未注圆角R2~R351.1.1塑件材料ABS的使用性能综合性能较好，冲击韧度、力学强度较高，尺寸稳定，耐化学性、电气性能良好；易于成形和机械加工，与有机玻璃的熔接性良好，可作双色成形塑件，且表面可镀铬。适于制作一般机械零件、减摩耐磨零件、传动零件和电信结构零件。1.1.2塑件材料ABS的加工特性无定型塑料，其品种很多，各品种的机电性能及成形特性也各有差异，应按品种确定成形方法及成形条件。吸湿性强，含水量应小于0.3%，必须充分干燥，要求表面光泽的塑件应要求长时间预热干燥。流动性中等，溢边料0.04mm左右（流动性比聚苯乙烯，AS差，但比聚碳酸酯、聚氯乙烯好）。比聚苯乙烯加工困难，宜取高料温、模温（对耐热、高抗冲击和中抗冲击型树脂，料温更宜取高）。料温对物性影响较大、料温过高易分解（分解温度为250℃左右，比聚苯乙烯易分解），对要求精度较高塑件，模温宜取50～60℃，要求光泽及耐热型料宜取60～80℃。注射压力应比加工聚苯乙烯稍高，一般用柱塞式注塑机时料温为180～230℃，注射压力为100～140MPa，螺杆式注塑机则取160～220℃，70～100MPa为宜。模具设计时要注意浇注系统，选择好进料口位置、形式。推出力过大或机械加工时塑件表面呈现“白色”痕迹（但在热水中加热可消6失）。脱模斜度宜取2℃以上。1.2塑件的成型工艺参数确定查手册得到ABS塑料的成型工艺参数：适用注射机类型螺杆式密度1.02～1.16g/cm3；收缩率0.3～0.8%；预热温度80C°～85C°，预热时间2～3h；料筒温度后段150C°～170C°，中段165C°～180C°，前段180C°～200C°；喷嘴温度170C°～180C°；模具温度50C°～80C°；注射压力60～100MPa；成型时间注射时间20～90s，保压时间0～5s，冷却时间20～120s。2模具的基本结构及模架选择2.1模具的基本结构2.1.1确定成型方法塑件采用注射成型法生产。使用侧浇口成型。72.1.2型腔布置塑件形状较简单，重量较轻，生产批量较大。所以应使用多型腔注射模具。考虑到塑件的侧面有Φ6.5mm的圆孔，需侧向抽芯，所以模具采用一模二腔、平衡布置。这样模具尺寸较小，制造加工方便，生产效率高，塑件成本较低。其布置如图所示。2.1.3确定分型面塑件分型面的选择应保证塑件的质量要求，因此分型面选择在A-A面，这样的选择使塑件便于取出，塑件大部分外表面光滑，同时侧向抽芯容易，而且塑件脱模方便。因此塑件选择如图所示的分型面。8分型面选择2.1.4选择浇注系统塑件采用侧浇口成型，其浇注系统如图所示。侧浇口直径为Φ2mm，侧浇口长度为2mm，头部球R1.5~2mm。分流道设计：采用半圆截面流道，其半径R为3~3.5mm。长度为20mm主流道设计：主流道为圆锥形，口部球面半径SR=12mm球面的配合高度h=3~5mm锥角α为6˚，上部直径与注射机喷嘴相配合下部直径Φ6~8mm。2.1.5确定推出方式选择推杆推出机构完成塑件的推出。92.1.6侧向抽芯机构塑件的侧面有Φ6.5mm的圆孔，因此模具应有侧向抽芯机构，由于抽出距离较短，抽出力较小，所以采用斜导柱、滑块抽芯机构。斜导柱装在定模板上，滑块装在动模板上。2.1.7选择成型设备注射机型